| 特性 TypicalProperties | 测试方法 ISO | 测试条件 Condition | 单位 Units | 一 般 级 | 食品接触级 | ||||||
| PN-108 | PN-118 | PN-128 | PN-138H | D-168 | D-178 | D-178HF | PN-107FG | ||||
| 熔体流动速率 MVR | 1133 | 200℃x5kg | ml/10min | 5.0 | 2.8 | 3.0 | 1.0 | 1.0 | 2.7 | 17.0 | 5.2 |
| 220℃x10kg | 51.0 | 34.0 | 35.0 | 11.0 | 11.0 | 30.0 | 183.0 | 58.0 | |||
| 质量密度 Mass Density | 1183 | 23℃ | g/cm³ | 1.07 | 1.07 | 1.07 | 1.08 | 1.08 | 1.07 | 1.07 | 1.06 |
| 拉伸强度 TensileStrength | 527 | 50mm/min | MPa | 67.0 | 71.0 | 72.0 | 81.0 | 81.0 | 75.0 | 57.0 | 65.0 |
| 延伸率Tensile Elongation | 527 | 50mm/min | % | 5.0 | 5.0 | 5.0 | 7.0 | 7.0 | 5.0 | 4.0 | 4.0 |
| 弯曲强度 FlexuralStrength | 178 | 2mm/min | MPa | 101 | 106 | 110 | 124 | 124 | 115 | 75 | 89 |
| 弯曲弹性模数 FlexuralModulus | 178 | 2mm/min | GPa | 3.4 | 3.4 | 3.6 | 3.7 | 3.7 | 3.5 | 3.4 | 2.6 |
| IZOD冲击强度 Izod Impact | 180 | 23℃ Notched | kJ/m² | 3.8 | 3.8 | 3.9 | 4.0 | 4.0 | 3.8 | 3.7 | 2.0 |
| Charpy冲击强度 CharpyImpact | 179 | 23℃ Notched | kJ/m² | 2.7 | 2.7 | 2.7 | 2.8 | 2.8 | 2.7 | 2.6 | 2.0 |
| 维氏软化温度 Vcat Softening Temp. | 306 | 50℃/Hr | ℃ | 105 | 105 | 107 | 108 | 108 | 105 | 104 | 104 |
| 热变形温度 HeatDefiection Temp. | 75-2 | unannealed | ℃ | 86 | 86 | 88 | 89 | 89 | 87 | 85 | 88 |
| annealed | ℃ | 97 | 97 | 99 | 100 | 100 | 97 | 98 | 99 | ||
| 燃烧性 Flammability | - | UL-94 | - | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB | 1.5mmHB |
| 产品特性与应用 | 一般射出 L100:本色 L125:极淡蓝 | 一般射出 L100:本色 L150:淡蓝 | 一般射出 L100:本色 L150:淡蓝 | 高强度 高耐化性 | 高强度 高耐化性 | 中强度耐化性 | 高流动级 | 食品接触级L125：极淡蓝 | |||